Rod Sintered AlNiCo 2 Speaker Magnet Bar Magnets For Sale

Delivery term:The date of payment from buyers deliver within days
  • Price:

    Negotiable

  • minimum:

  • Total supply:

  • Delivery term:

    The date of payment from buyers deliver within days

  • seat:

    Beijing

  • Validity to:

    Long-term effective

  • Last update:

    2017-12-30 16:47

  • Browse the number:

    264

Send an inquiries
+
Xiamen Jingxin Imp. & Exp. Co.,Ltd
Contactaixin:

Contactaixin:

jingxin(Mr.)  

Email:

telephone:

phone:

Area:

Beijing

Address:

Xiamen Jingxin Imp. & Exp. Co.,Ltd

Website:

http://www.astrongmagnets.com/ http://jingxin.bokess.com/

+

AlNiCo magnet is the earliest developed permanent magnet material in 1930s, which is made of an alloy of aluminum, nickel, cobalt, iron and other trace metals. At that time, it had best magnetic properties and low temperature coefficient, so it widely used in permanent magnet motor. After 1960s, with the development of ferrite magnets and NdFeB magnet, the AlNiCo magnets were replace by them in the fields of permanent magnet motor step and step.

According to the different production process is divided into Sintered AlNiCo and Cast AlNiCo. Sintered Alnico magnet is manufactured using a powder metallurgy process which uses controlled atmosphere, high temperature sintering to produce near net shape parts. These may range in size from as little as .05g to 150g. Semi automated production enables adjustment of materials, and processing allows either a standard range of magnetic properties or individually tailored alloys to meet customer specifications.

Sintered AlNiCo offer slightly lower magnetic properties but better mechanical characteristics than the cast AlNiCo. Sintered AlNiCo magnets are most suitable in small sizes. The sintering process is well suited to large volume production, and results in parts which are structurally stronger than cast magnets. Relatively close tolerances can be achieved without grinding.


Typical magnetic properties of Sintered AlNiCo:

Equivalent MMPA Class

Grade

Br

Hcb

(BH)max

α(Br)

Tc

Tw(Max)

Density

mT

Gs

KA/m

Oe

KJ/m3

MGOe

%/℃

g/cm3

S.Alnico 3

FLN8

550

5500

42

530

9

1.13

-0.022

760

450

6.7

S.Alnico 2

FLNG12

700

7000

48

600

12.4

1.55

-0.014

810

450

7

S.Alnico 7

FLNGT18

580

5800

90

1130

18

2.2

-0.02

850

500

7.2

S.Alnico 5

FLNG34

1100

11000

48

600

34

4.25

-0.016

890

500

7.2

S.Alnico 6

FLNGT28

1000

10000

56

700

28

3.5

-0.02

850

500

7.2

S.Alnico 8

FLNGT38

800

8000

100

1250

32

4

-0.02

850

500

7.2

FLNGT42

850

8500

110

1380

38

4.75

-0.02

850

500

7.2

S.Alnico8HC

FLNGT33J

680

6800

140

1750

36

4.5

-0.025

850

500

7.2